The article, a room temperature vulcanized silicone rubber material properties
the room temperature vulcanized silicone rubber is a widely dosage of organic silicone industry of silicone rubber, RTV for short, as early as ten years ago at room temperature vulcanization silicone rubber in China has reached 300000 tons of demand, it is given priority to with the construction industry, used for glass adhesive, sealant, indoor decoration, doors and Windows sealed majority, as the industry currently USES gradual expansion and the innovation of the product research and development to its rapid development, and performance specifications of the products or not change, you have to know its material performance?
1, table dry time means rtv-i silicone products exposed to atmospheric environment curing process, the fingers touch the appearance, viscosity of lost time. Under the condition of the general refers to the specifications, silicone rubber surface sealant extrusion air buy, appearance is not hands time distance.
2, curing depth refers to the standard conditions, the silicone rubber surface sealant in the fixed mold, a certain period of time after the glue, silicone rubber surface sealant outside-in curing rubber thickness, such as: 2 ~ 3 mm / 24 h, 0. 6 mm/h, etc.
3, extrusion ( Defined in accordance with the specification ASTMC1183)
in accordance with ASTM C1183 specification request, under the condition of the specification, using Semco tubes and specific cement ( 3 in diameter. 2毫米) , under the condition of specific pressure, extrusion of weight per unit time is called out.
4, instant sealing pressure
refers to the silicone rubber surface sealant at a certain diameter sizing in the flange plate of plane, then immediately closed, control of thickness of the rubber has a reasonable, then in accordance with certain rate exert pressure, the biggest pressure for the instant sealing pressure to accept.
5, oil curing characteristics is refers to the silicone rubber products planar sealant in the fixed mold, then the mold in the oil, recorded in the silicone rubber surface sealant outside-in curing within a certain amount of time to represent the thickness of the silicone rubber surface sealant solidification features of oil.
6, drying time shear strength insist rate
is used to glue the shear specimens under the specific conditions of high temperature, high humidity place after a certain amount of time, then stop fold glue, the specification is placed under the condition of 168 h stop curing and test its shear strength, and with the specification under the condition of direct bonding shear strength of cured 168 h test stop comparison, calculation strength rate.
7, the thermal stability of the curing of the
it is to point to will not plane of silicone sealant in the environment of high temperature curing time, and then under the condition of specification can still curing, silicone rubber surface sealant in the temperature is stable. Such as sealant temperature 100 ℃ or higher thermal stability refers to not curing sealant after 100 ℃ heating can still continue to curing.
depending on the phenyl content in silicone rubber, it can be divided into low phenyl, phenyl and high phenyl silicone rubber. Crystallization occurs when the rubber or close to the glass transition point or that the overlap of the two, both can lead to stiffness of rubber. Introducing the right amount of mass groups in the regularity of the polymer chain is damaged, can reduce the crystallization temperature of polymer, due to the introduction of mass groups at the same time change the force between the polymer molecules, so it can change the glass transition temperature.
low phenyl silicone rubber ( C6H5/Si=6~11%） Is due to the above reason has good low temperature resistance, and has nothing to do with phenyl monomer type used. The brittleness temperature for - vulcanized rubber 120 ℃, it is now the best rubber performance at low temperature. The advantages of low phenyl silicone rubber and vinyl silicone rubber, and the cost is not high, therefore has a tendency to replace the vinyl silicone rubber. When greatly improve the content of phenyl will make molecular chain rigidity increases, thus resulting in a loss of cold tolerance and flexibility, but ablation resistance and radiation resistance will be improved, phenyl content of C6H5 / Si = 20 ~ 34% of phenyl silicone rubber has the characteristics of ablation resistant, high phenyl silicone rubber ( C6H5/Si=35~50%） Excellent resistance to radiation performance.
Foshan taihai rubber and plastic co., LTD. outfits our businesses with rubber washers because they're relatively affordable and highly customizable.
Foshan taihai rubber and plastic co., LTD. is working with the best teams, aligned with international standards and practices to focus on R&D and manufacture of products, and are continuously launching new products in the market. Get to know us at TaiHai Rubber Products.
The best way to determine the ideal strategy of rubber washers is to continually test and refine your selling and marketing tactics.
Foshan taihai rubber and plastic co., LTD. has never compromised on the quality and the services provided to the customer.
Foshan taihai rubber and plastic co., LTD. provides professional , technology and human expertise clients need to find trusted answers. Go to TaiHai Rubber Products for answers.